Thermoluminescent characteristics of LiF:Mg, Cu, P and CaSO4:Dy for low dose measurement.

Thermoluminescence (TL) characteristics for LiF:Mg, Cu, P, and CaSO4:Dy under the homogeneous field of X-ray beams of diagnostic irradiation and its verification using thermoluminescence dosimetry are presented. The irradiation were performed utilizing a conventional X-ray equipment installed at the Hospital Juárez Norte of México. Different thermoluminescence characteristics of two material were studied, such as batch homogeneity, glow curve, linearity, detection threshold, reproducibility, relative sensitivity and fading. Materials were calibrated in terms of absorbed dose to the standard calibration distance and they were positioned in a generic phantom. The dose analysis, verification and comparison with the measurements obtained by the TLD-100 were performed. Results indicate that the dosimetric peak appears at 202°C and 277.5°C for LiF:Mg, Cu, P and CaSO4:Dy, respectively. TL response as a function of X-ray dose showed a linearity behavior in the very low dose range for all materials. However, the TLD-100 is not accurate for measurements below 4mGy. CaSO4:Dy is 80% more sensitive than TLD-100 and it show the lowest detection threshold, whereas LiF:Mg, Cu, P is 60% more sensitive than TLD-100. All materials showed very good repeatability. Fading for a period of one month at room temperature showed low fading LiF:Mg, Cu, P, medium and high for TLD-100 and CaSO4:Dy. The results suggest that CaSO4:Dy and LiF:Mg, Cu, P are suitable for measurements at low doses used in radiodiagnostic.

Thermoluminescent dosimeters for low dose X-ray measurements.

The response of TLD-100, CaSO4:Dy and LiF:Mg,Cu,P for a range of X-ray low dose was measured. For calibration, the TLDs were arranged at the center of the X-ray field. The dose output of the X-ray machine was determined using an ACCU-Gold. All dosimeters were exposed at the available air kerma values of 14.69 mGy within a field 10×10 cm(2) at 80 cm of SSD. Results of LiF:Mg,Cu,P X-ray irradiated showed 4.8 times higher sensitivity than TLD-100. Meanwhile, TL response of CaSO4:Dy exposed at the same dose was 5.6 time higher than TLD-100. Experimental results show for low dose X-ray measurements a better linearity for LiF:Mg,Cu,P compared with that of TLD-100. CaSO4:Dy showed a linearity from 0.1 to 60 mGy.

Thermoluminescent characterization of HfO2:Tb3+ synthesized by hydrothermal route.

Thermo and photoluminescent properties of nanoparticles (NPs) of hafnium oxide (HfO2), both intrinsic and doped with terbium (Tb(3+)) are reported. The NPs of HfO2 were synthesized by hydrothermal route, using hafnium tetrachloride (HfCl4) and terbium chloride hexahydrated (TbCl3∙6H2O) as precursors and sodium hydroxide (NaOH) to adjust the pH. Deionized water was used as solvent in all cases. The synthesis was carried out at different dopant concentrations from 0 to 20 at% of terbium with respect to the amount of hafnium in the precursor solution. The temperature of hydrothermal treatment was 200 °C and 80 min of reaction time. X-ray diffraction results show that at terbium concentrations higher than 15 at% the HfO2 nanoparticles have a crystalline structure corresponding to the tetragonal phase. Thermoluminescent (TL) characterization was performed after 5 min irradiation of the samples with ultraviolet light of 200 nm wavelength. The highest TL emission was observed on samples with 7 at% of Tb, with the TL peak centered at 128 °C. Thermoluminescence analysis shows behavior associated with second-order kinetics with activation energy of 0.49 eV. Photoluminescent spectrum present the characteristics (5)D4→(7)FJ (J=3-6) terbium ion electronic transitions lines centered on 489 nm, 543 nm, 584 nm and 622 nm.